Pls Scan our customer service whatsappJoint bearing
Design Introduction
The POLYESTER LUBRICATION series bearings in Channov product series are continuously wound with glass fiber and epoxy resin material (bearing layer), filled with PTFE fiber and high strength fiber internal lubricant and high temperature epoxy resin as sliding layer, so as to form a natural concentric high strength bearing without joint and overlap This high-strength laminate structure allows bearing wall thickness of only (1.59mm-3.18mm), reducing product size and bearing weight during assembly such composite bearings exhibit extremely low friction coefficients and high bearing capacity
| Material properties | Standard | g/cm3 | Value |
| Specific Gravity | ISO1183 | g/cm3 | 1.95 |
| Max. water absorption | ISO62 | % | 0.1 |
| Max. PV(dry) | ITS026 | N/mm2 Xm/s | 1.8 |
| Friction Coefficient | ITS025 | μ | 0.03~0.12 |
| Long-term Operating Temperature | ITS029 | °C | 160 |
| Short-term Operating Temperature | ITS029 | °C | 180 |
| Minimum Operating Temperature | ITS029 | °C | -100 |
| Max.Speed | ITS032 | m/s | 0.2 |
| Tensile Strength | ITS033 | Mpa | 420 |
| Max.Static load | ITS027 | Mpa | 240 |
| Max.Dynamic load | ITS028 | Mpa | 140 |
| Shore Hardness | ITS868 | D | 96 |
| Coefficient of linear thermal expansion | ISO11359 | 10-5 *K-1 | 13 |
Einsatzgebiete
| Widely used in various engineering machinery, construction machinery, medical machinery, packaging machinery, food machinery, ship machinery, new energy, aerospace fields, electrical and electronic fields |